0Cr21Al4 resistance wire is a type of iron chromium aluminum alloy resistance wire, which has good high-temperature stability and oxidation resistance, and is therefore widely used in many fields.
By being applied in the chemical industry, 0Cr21Al4 resistance wire provides crucial support for the safe and efficient operation of chemical processes and plays an important role in various chemical applications.
0Cr21Al4 resistance wire is extensively used as heating elements in the chemical industry for heating liquids, gases, or solids to facilitate chemical reactions or maintain specific temperatures.
- Heating furnaces and heat treatment equipment
0Cr21Al4 resistance wire is used in chemical heating furnaces and heat treatment equipment for heating and treating various chemical substances and materials.
- Resistance heating steam generators
0Cr21Al4 resistance wire is used in resistance heating steam generators to heat water into steam for driving distillation, drying, or heating operations in chemical processes.
- Resistance heating reaction vessels
0Cr21Al4 resistance wire is used as resistance heaters in chemical reaction vessels to control and facilitate chemical reactions.
- Sensors and control systems
0Cr21Al4 resistance wire is used as sensor elements in chemical processes and resistor components in control systems to monitor and control parameters such as temperature, pressure, or liquid level.
- Ferrous Chromium Aluminum alloy performance tables
| Alloy Nomenclature Performance | 1Cr13Al4 | 0Cr25Al5 | 0Cr21Al6 | 0Cr23Al5 | 0Cr21Al4 | 0Cr21Al6Nb | 0Cr27Al7Mo2 |
| Main Chemical composition | Cr | 12.0-15.0 | 23.0-26.0 | 19.0-22.0 | 20.5-23.5 | 18.0-21.0 | 21.0-23.0 | 26.5-27.8 |
| Al | 4.0-6.0 | 4.5-6.5 | 5.0-7.0 | 4.2-5.3 | 3.0-4.2 | 5.0-7.0 | 6.0-7.0 |
| Re | opportune | opportune | opportune | opportune | opportune | opportune | opportune |
| Fe | Rest | Rest | Rest | Rest | Rest | Rest | Rest |
| | | | | | | Nb0.5 | Mo1.8-2.2 |
| Max. continuous service temp. of element(°C) | 950 | 1250 | 1250 | 1250 | 1100 | 1350 | 1400 |
| Resistivity at 20ºC(μΩ·m) | 1.25 | 1.42 | 1.42 | 1.35 | 1.23 | 1.45 | 1.53 |
| Density(g/cm3) | 7.4 | 7.1 | 7.16 | 7.25 | 7.35 | 7.1 | 7.1 |
| Thermal conductivity(KJ/m·h·ºC) | 52.7 | 46.1 | 63.2 | 60.2 | 46.9 | 46.1 | |
| Coefficient of lines expansion(α×10-6/ºC) | 15.4 | 16 | 14.7 | 15 | 13.5 | 16 | 16 |
| Melting point approx.( ºC) | 1450 | 1500 | 1500 | 1500 | 1500 | 1510 | 1520 |
| Tensile strength(N/mm2) | 580-680 | 630-780 | 630-780 | 630-780 | 600-700 | 650-800 | 680-830 |
| Elongation at rupture(%) | >16 | >12 | >12 | >12 | >12 | >12 | >10 |
| Variation of area(%) | 65-75 | 60-75 | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 |
| Repeat Bending frequency(F/R) | >5 | >5 | >5 | >5 | >5 | >5 | >5 |
| Hardness(H.B.) | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 |
| Continuous Servicetime(Hours/ ºC) | -- | ≥80/1300 | ≥80/1300 | ≥80/1300 | ≥80/1250 | ≥50/1350 | ≥50/1350 |
| Micrographic structure | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite |
| Magnetic properties | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic |